Materials, Vol. 12, Pages 1675: Effect of Air Oxidation on Texture, Surface Properties and Dye Adsorption of Wood-Derived Porous Carbon Materials (Materials)

Hierarchical porous carbon materials made from cork were fabricated using a facile and green method combined with air activation, without any templates and chemical agents. The influence of air activation on the texture and other surface characteristics of the carbon materials were evaluated by various characterization techniques. Results indicate that air oxidation can effectively improve the surface area and the hierarchical porous structure of carbon materials, as well as increase the number of oxygen-containing functional groups on the carbon surface. The specific surface area and the pore volume of the carbon material activated by air at 450 °C (C800-M450) can reach 580 m2/g and 0.379 cm3/g, respectively. These values are considerably higher than those for the non-activated material (C800, 376 m2/g, 0.201 cm3/g). The contents of the functional groups (C–O, C=O and O–H) increased with rising activation temperature. After air activation, the adsorption capacity of the carbon materials for methylene blue (MB) and methyl orange (MO) was increased from 7.7 and 6.4 mg/g for C800 to 312.5 and 97.1 mg/g for C800-M450, respectively. The excellent dye removal of the materials suggests that the porous carbon obtained from biomass can be potentially used for wastewater treatment.